Concrete Technology 2/4
Aalto UniversitySchool of EngineeringDepartment of Civil and Structural EngineeringBuilding Materials Technology
![Page 2: Concrete Technology 2/4 - Aalto · Concrete Technology 2/4 Aalto University School of Engineering Department of Civil and Structural Engineering Building Materials Technology](https://reader033.vdocuments.pub/reader033/viewer/2022051602/5ae574737f8b9a8b2b8be1bc/html5/thumbnails/2.jpg)
Hydration in a closed systemWater is not transferred with the surroundingsVariables v volume fraction (0…1)
hydration degree (0…1)1- solid concentration (0…1)
Volume of unhydrated cement
Solid volume of the gel
Concrete Technology 2
)1)(1( αθ −−=cv
( ) wcgsv ραθ−ρ−+αθ−≅ /126,0)25,01()1(
αθ−≅ )1(6,1gsv
![Page 3: Concrete Technology 2/4 - Aalto · Concrete Technology 2/4 Aalto University School of Engineering Department of Civil and Structural Engineering Building Materials Technology](https://reader033.vdocuments.pub/reader033/viewer/2022051602/5ae574737f8b9a8b2b8be1bc/html5/thumbnails/3.jpg)
Concrete Technology 2
Volume of gel water
Volume of capillary water
Volume of the contraction pores
vgw c w≅ ⋅ −0 75 0 26 1, , ( ) /ρ θ α ρ
vgw ≈ −0 6 1, ( )θ α
vkw c w≅ − ⋅ − − −θ ρ θ α ρ θ α0 26 1 0 6 1, ( ) / , ( )vkw ≅ − −θ θ α1 4 1, ( )
vp c w≅ ⋅ −0 25 0 26 1, , ( ) /ρ θ α ρvp ≈ −0 2 1, ( )θ α
![Page 4: Concrete Technology 2/4 - Aalto · Concrete Technology 2/4 Aalto University School of Engineering Department of Civil and Structural Engineering Building Materials Technology](https://reader033.vdocuments.pub/reader033/viewer/2022051602/5ae574737f8b9a8b2b8be1bc/html5/thumbnails/4.jpg)
Concrete Technology 2
Transfer of water can take place with the environment
The water volume transferred between the environment andstructure (cement + water) is denoted by v the formulaeof capillary water and porosity are changed
Hydration in an open system
structuretheofinsidefromdiffusionofratesurfacethefromnevaporatioofrate
vvvv kwkw ∆∆αθθ +=+−−≅ )1(4,1'
vvvv pp ∆∆αθ −=−−≅ )1(2,0'
pkw vvv ≤≤− ∆
![Page 5: Concrete Technology 2/4 - Aalto · Concrete Technology 2/4 Aalto University School of Engineering Department of Civil and Structural Engineering Building Materials Technology](https://reader033.vdocuments.pub/reader033/viewer/2022051602/5ae574737f8b9a8b2b8be1bc/html5/thumbnails/5.jpg)
Conversion of the volume variables to weight based variables(kg/ concrete m3)
-total volume of the system
-the volume variables are multiplied by the totalvolume of the system
Concrete Technology 2
332,032,0
11
mlQQ
cvQ
cvQ
QQv
wcc
wcc
w
w
c
ctot
+≈
+≅
+=+=
ρρρρ
![Page 6: Concrete Technology 2/4 - Aalto · Concrete Technology 2/4 Aalto University School of Engineering Department of Civil and Structural Engineering Building Materials Technology](https://reader033.vdocuments.pub/reader033/viewer/2022051602/5ae574737f8b9a8b2b8be1bc/html5/thumbnails/6.jpg)
Volume of hydration productsInitial porosity
Volume of unhydrated cement
Concrete Technology 2
c
wcw
cw
ρ
ρθ+
=
)1()1( αθ −⋅−=cv
![Page 7: Concrete Technology 2/4 - Aalto · Concrete Technology 2/4 Aalto University School of Engineering Department of Civil and Structural Engineering Building Materials Technology](https://reader033.vdocuments.pub/reader033/viewer/2022051602/5ae574737f8b9a8b2b8be1bc/html5/thumbnails/7.jpg)
Solid volume of the gel
Volume of gel water
Volume of capillary water
Volume of the contraction pores
Concrete Technology 2
αθ ⋅−⋅= )1(6,1gsv
αθ ⋅−⋅= )1(6,0gwv
αθθ ⋅−⋅−= )1(4,1kwv
αθ ⋅−⋅= )1(2,0pv
![Page 8: Concrete Technology 2/4 - Aalto · Concrete Technology 2/4 Aalto University School of Engineering Department of Civil and Structural Engineering Building Materials Technology](https://reader033.vdocuments.pub/reader033/viewer/2022051602/5ae574737f8b9a8b2b8be1bc/html5/thumbnails/8.jpg)
Concrete Technology 2
Maximum degree of hydration
1. No external water
vkw=0
2. Wet curing
1)1(4,1max ≤
−⋅=
θθα
vkw+vp=0 1)1(2,1max ≤
−⋅=
θθα
![Page 9: Concrete Technology 2/4 - Aalto · Concrete Technology 2/4 Aalto University School of Engineering Department of Civil and Structural Engineering Building Materials Technology](https://reader033.vdocuments.pub/reader033/viewer/2022051602/5ae574737f8b9a8b2b8be1bc/html5/thumbnails/9.jpg)
Concrete Technology 2
![Page 10: Concrete Technology 2/4 - Aalto · Concrete Technology 2/4 Aalto University School of Engineering Department of Civil and Structural Engineering Building Materials Technology](https://reader033.vdocuments.pub/reader033/viewer/2022051602/5ae574737f8b9a8b2b8be1bc/html5/thumbnails/10.jpg)
Concrete Technology 2
Hydration of condensed silica fume-chemical shrinkage is 22 ml/100 g silica fume-amount of gel water is 0.50 g/ g silica fume-water amount consumed in the reaction 0 g/ g silica
Densities of the components-ρc= 3100-3150 kg/m3
-ρw= 1000 kg/m3
-ρs= 2200 kg/m3
Volume of hydration products when condensedsilica fume is applied
![Page 11: Concrete Technology 2/4 - Aalto · Concrete Technology 2/4 Aalto University School of Engineering Department of Civil and Structural Engineering Building Materials Technology](https://reader033.vdocuments.pub/reader033/viewer/2022051602/5ae574737f8b9a8b2b8be1bc/html5/thumbnails/11.jpg)
Concrete Technology 2
Initial porosity
coefficient
cs
cw
cw
s
w
c
w ⋅++=
ρ
ρ
ρ
ρθ
csk
⋅+=
4,11
1
![Page 12: Concrete Technology 2/4 - Aalto · Concrete Technology 2/4 Aalto University School of Engineering Department of Civil and Structural Engineering Building Materials Technology](https://reader033.vdocuments.pub/reader033/viewer/2022051602/5ae574737f8b9a8b2b8be1bc/html5/thumbnails/12.jpg)
Concrete Technology 2
Volume of unhydrated cement
Solid volume of the gel
Volume of gel water
Volume of capillary water
)1()1( αθ −⋅−⋅= kvc
αθ ⋅−⋅+⋅= )1()7,06,1(cskvgs
αθ ⋅−⋅+⋅= )1()6,16,0(cskvgw
αθθ ⋅−⋅+⋅−= )1()6,14,1(cskvkw
![Page 13: Concrete Technology 2/4 - Aalto · Concrete Technology 2/4 Aalto University School of Engineering Department of Civil and Structural Engineering Building Materials Technology](https://reader033.vdocuments.pub/reader033/viewer/2022051602/5ae574737f8b9a8b2b8be1bc/html5/thumbnails/13.jpg)
Volume of the contraction pores
Volume of the unreacted condensed silica fume
Maximum degree of hydration
1. No external water
vkw=0
Concrete Technology 2
αθ ⋅−⋅+⋅= )1()7,02,0(cskv p
)1()1(4,1 αθ −⋅−⋅⋅⋅=cskvs
1)1()6,14,1(
max ≤−⋅+⋅
=θ
θα
csk
![Page 14: Concrete Technology 2/4 - Aalto · Concrete Technology 2/4 Aalto University School of Engineering Department of Civil and Structural Engineering Building Materials Technology](https://reader033.vdocuments.pub/reader033/viewer/2022051602/5ae574737f8b9a8b2b8be1bc/html5/thumbnails/14.jpg)
2. Wet curing
vkw+vp=0
Concrete Technology 2
1)1()9,02,1(
max ≤−⋅+⋅
=θ
θα
csk
![Page 15: Concrete Technology 2/4 - Aalto · Concrete Technology 2/4 Aalto University School of Engineering Department of Civil and Structural Engineering Building Materials Technology](https://reader033.vdocuments.pub/reader033/viewer/2022051602/5ae574737f8b9a8b2b8be1bc/html5/thumbnails/15.jpg)
Capillary pores-represent that part of the total volume of the cement pastethat is not filled by the hydration products-volume of capillary pores is dependent on water-cementratio and degree of hydrationVolume proportions during different phases of hydration
If v/c > 0,38 - 0,42, the hydration products of cement pastecannot fill all of the capillary pores.Capillary pores- have approximately diameter < 1,3 µm- shape is variable- can be connected with each other
Concrete Technology 2
![Page 16: Concrete Technology 2/4 - Aalto · Concrete Technology 2/4 Aalto University School of Engineering Department of Civil and Structural Engineering Building Materials Technology](https://reader033.vdocuments.pub/reader033/viewer/2022051602/5ae574737f8b9a8b2b8be1bc/html5/thumbnails/16.jpg)
- are distributed randomly in the cement gel- have a major effect on permeability and freeze-thaw
durabilityAs hydration proceeds the connectivity to other capillarypores can be broken and they are connected to each otheronly through gel pores- v/c -ratio- curing in wet conditionsThe hydration degree and water-cement ratio which makesit possible to break the connectivity of the capillary poresare- if v/c ≥ 0,7 not even complete hydration degree enables
the interception
Concrete Technology 2
![Page 17: Concrete Technology 2/4 - Aalto · Concrete Technology 2/4 Aalto University School of Engineering Department of Civil and Structural Engineering Building Materials Technology](https://reader033.vdocuments.pub/reader033/viewer/2022051602/5ae574737f8b9a8b2b8be1bc/html5/thumbnails/17.jpg)
Concrete Technology 2
- when cement is finely ground v/c < ∼0,8- applying coarse cements v/c < 0,7
The average curing time (hardening time) for capillarypores to break a continuous pore system
v/c Time0.40 3 d0.45 7 d0.50 14 d0.60 6 months0.70 1 year
>0.70 impossible
![Page 18: Concrete Technology 2/4 - Aalto · Concrete Technology 2/4 Aalto University School of Engineering Department of Civil and Structural Engineering Building Materials Technology](https://reader033.vdocuments.pub/reader033/viewer/2022051602/5ae574737f8b9a8b2b8be1bc/html5/thumbnails/18.jpg)
Concrete is not usually considered to be proper if capillarypores form a continuous pore system.
Gel pores- spaces between gel particles- φ ≅ 15...20 Å (Å = 10 -10 m)- a decade larger compared to water molecules ⇒ they are
affected by partial pressure and mobility of water vapor -- the volume content of gel pores is 28 % of gel total
volume depending on the hardening conditions.
Concrete Technology 2
![Page 19: Concrete Technology 2/4 - Aalto · Concrete Technology 2/4 Aalto University School of Engineering Department of Civil and Structural Engineering Building Materials Technology](https://reader033.vdocuments.pub/reader033/viewer/2022051602/5ae574737f8b9a8b2b8be1bc/html5/thumbnails/19.jpg)
Concrete Technology 2
-the volume content of gel pores is somewhat dependenton cement type but does not depend on
-water-cement ratio nor-hydration degree
⇒ Hydration does not affect on the previously generatedhydration products and the gel composition isinvariant of the age at which it is forming
-the surface area of the cement gel is about 200 000m2/kg, while the surface area of unhydrated cement isabout 300 m2/kg
-the surface area of cement gel which has hydrated inhigh temperature is about 7000 m2/kg ⇒ Thedimensions and morphology of the hydration productsare quite different ⇒ the structure is microcrystalline
![Page 20: Concrete Technology 2/4 - Aalto · Concrete Technology 2/4 Aalto University School of Engineering Department of Civil and Structural Engineering Building Materials Technology](https://reader033.vdocuments.pub/reader033/viewer/2022051602/5ae574737f8b9a8b2b8be1bc/html5/thumbnails/20.jpg)
Supplementary binders
Fly ash-coal ash-peat ash pozzolanic reaction-wood ash
Commonly used in Finland is coal ash produced in heat andelectricity power plants
-2-15 % unburnt coal residues-collected from the exhaust gases-bottom ash not suitable
Concrete Technology 2
![Page 21: Concrete Technology 2/4 - Aalto · Concrete Technology 2/4 Aalto University School of Engineering Department of Civil and Structural Engineering Building Materials Technology](https://reader033.vdocuments.pub/reader033/viewer/2022051602/5ae574737f8b9a8b2b8be1bc/html5/thumbnails/21.jpg)
Composition of coal ash in a typical power plant
Concrete Technology 2
Component Variation area%
Average value%
Requirement
SiO2 40 - 50 48(S + A+ F)Together> 70 %
Al2O3 20 - 30 23
Fe2O3 8 – 13 10
CaO 4 – 10 7
MgO 3 – 6 4 5.0 %
Na2O+K2O 1 - 4 2.5
SO3 0.5 – 1.5 0.8 2.5 %
Cl- - 0.03 0.1 %
Loss of ignition 0.5 - 8 2 8 %
![Page 22: Concrete Technology 2/4 - Aalto · Concrete Technology 2/4 Aalto University School of Engineering Department of Civil and Structural Engineering Building Materials Technology](https://reader033.vdocuments.pub/reader033/viewer/2022051602/5ae574737f8b9a8b2b8be1bc/html5/thumbnails/22.jpg)
Maximum allowable supplementary binder amounts
Concrete Technology 2
Seosaineiden käytön sallitut enimmäismäärät riippuenrasitusluokista ja käytettävästä sementistä on esitetty taulukossa4.4.
Taulukko 4.4 Betonin valmistuksessa suurimmat sallitutseosainelisäykset lasketaan seuraavista kaavoista, joissaQII on sementin sisältämät seosaineet [%].
Rasitusluokka Suurin sallittu seosainelisäys [%]Masuunikuona Lentotuhka Silika1)
X0XC1…XC3XS1XD1, XA1
10020
−,
Q-100 II
100650
−,
Q-100 II
9Q-100 II
XF1, XF3
100750
−,
Q-100 IIXC4,XS2, XS3XD2, XD3
10080
−,
Q-100 II
XF2, XF4 10050
−,
Q-100 II
14Q-100 II
1) Lisäksi on varmistuttava, että syntyvän sideaineseoksenklinkkeripitoisuus on vähintään 65 % rasitusluokissa X0, XC1…XC3, XS1, XD1 ja XA1 ja 80 % muissa rasitusluokissa.
![Page 23: Concrete Technology 2/4 - Aalto · Concrete Technology 2/4 Aalto University School of Engineering Department of Civil and Structural Engineering Building Materials Technology](https://reader033.vdocuments.pub/reader033/viewer/2022051602/5ae574737f8b9a8b2b8be1bc/html5/thumbnails/23.jpg)
Particle size distribution and properties-between the distributions of fillers and cement-50 – 70 % spherical ash particles, part of which are hollow-density of the solid content 2.2 kg/m3
-particle density 1.4 – 1.5 kg/m3
-dusty-pozzolanic binder having efficiency coefficient of 0.2 – 0.4 incompressive strength compared to Portland cementUtilization of coal fly ash1. Raw material in clinker production
-intermediate product-already in fine particle form-residual coal acts as additional energy source
Concrete Technology 2
![Page 24: Concrete Technology 2/4 - Aalto · Concrete Technology 2/4 Aalto University School of Engineering Department of Civil and Structural Engineering Building Materials Technology](https://reader033.vdocuments.pub/reader033/viewer/2022051602/5ae574737f8b9a8b2b8be1bc/html5/thumbnails/24.jpg)
2. As a supplementary binder with cement-maximum content in CEM IIA is 10 %-maximum content in CEM IIB is 35 %-maximum content with CEM I is 60 %-mixed with cement before or after grinding
3. Substitute for natural filler-aggregate-pneumatic transport and water tight filler silos-good homogeneity
Concrete Technology 2
![Page 25: Concrete Technology 2/4 - Aalto · Concrete Technology 2/4 Aalto University School of Engineering Department of Civil and Structural Engineering Building Materials Technology](https://reader033.vdocuments.pub/reader033/viewer/2022051602/5ae574737f8b9a8b2b8be1bc/html5/thumbnails/25.jpg)
Properties in fresh concreteCoal fly ash improves
-workability-pumpability-cohesion
Good quality coal fly ash-possesses a small loss of ignition and fine particle size-decreases water demand of the mix
When coal fly ash is applied-concrete becomes denser-air content is decreased-color is “greener”-hydration heat is decreased
Concrete Technology 2
![Page 26: Concrete Technology 2/4 - Aalto · Concrete Technology 2/4 Aalto University School of Engineering Department of Civil and Structural Engineering Building Materials Technology](https://reader033.vdocuments.pub/reader033/viewer/2022051602/5ae574737f8b9a8b2b8be1bc/html5/thumbnails/26.jpg)
-decreases cement content-reacts with and binds calcium hydroxide-improves durability in some cases
Properties in hardened concrete-latent hydraulic properties (pozzolanic reaction withCa(OH)2, 1kg fly ash binds 875 g of Ca(OH)2)
-when used as supplementary binder as a replacementof cement early age strength decreases and finalstrength increases-when used as a filler the pozzolanic reactionimproves strength (not necessarily 28 d strength)-heat treatment improves hardening rate (even earlystrength)
Concrete Technology 2
![Page 27: Concrete Technology 2/4 - Aalto · Concrete Technology 2/4 Aalto University School of Engineering Department of Civil and Structural Engineering Building Materials Technology](https://reader033.vdocuments.pub/reader033/viewer/2022051602/5ae574737f8b9a8b2b8be1bc/html5/thumbnails/27.jpg)
-improves chemical durability of concrete, especiallydurability against sulfates-decreases the susceptibility for alkali-aggregatereaction and improves the volume stability ofcements containing too large amounts of MgO
Large fly ash content decreases Ca(OH)2 content in hydratedconcrete which increases the risk of reinforcement corrosion.
Maximum fly ash content is restricted to 60 % of Portlandcement (CEM I).
Concrete Technology 2
![Page 28: Concrete Technology 2/4 - Aalto · Concrete Technology 2/4 Aalto University School of Engineering Department of Civil and Structural Engineering Building Materials Technology](https://reader033.vdocuments.pub/reader033/viewer/2022051602/5ae574737f8b9a8b2b8be1bc/html5/thumbnails/28.jpg)
Large coal content in fly ash-diminishes the pozzolanic reaction-increases water demand-causes color variations-coal particles absorb admixtures, for example, air-entraining admixture dosage must be increased 1.2 –2 fold
Fly ash and admixtures-plasticizers and retarding plasticizers generatehigher 91 d strength and decrease water segregation,Young’s modulus, and 90 d shrinkage. Setting timeincreases by 1 – 2 hours.
Concrete Technology 2
![Page 29: Concrete Technology 2/4 - Aalto · Concrete Technology 2/4 Aalto University School of Engineering Department of Civil and Structural Engineering Building Materials Technology](https://reader033.vdocuments.pub/reader033/viewer/2022051602/5ae574737f8b9a8b2b8be1bc/html5/thumbnails/29.jpg)
Advantages of fly ash as a filler-diminished water demand-particle composition is finer which diminishes watersegregation-smaller density
Disadvantages of fly ash-quality control-difficulties in quality variations-cumbersome handling compared to natural fillers-seasonal variation which causes storage needs-transport costs-additional dosage amount of admixtures
Concrete Technology 2
![Page 30: Concrete Technology 2/4 - Aalto · Concrete Technology 2/4 Aalto University School of Engineering Department of Civil and Structural Engineering Building Materials Technology](https://reader033.vdocuments.pub/reader033/viewer/2022051602/5ae574737f8b9a8b2b8be1bc/html5/thumbnails/30.jpg)
Utilization of wood fly ash
• Recycled material from energy production of wood andpaper industry
• Annual production about 300 000 tons in Finland• Raw material consists of bark, saw dust, and different
fiber or leftover sludges• Has similar properties as fly ash produced from coal in
electricity and heat production
Concrete Technology 2
![Page 31: Concrete Technology 2/4 - Aalto · Concrete Technology 2/4 Aalto University School of Engineering Department of Civil and Structural Engineering Building Materials Technology](https://reader033.vdocuments.pub/reader033/viewer/2022051602/5ae574737f8b9a8b2b8be1bc/html5/thumbnails/31.jpg)
Concrete Technology 2
![Page 32: Concrete Technology 2/4 - Aalto · Concrete Technology 2/4 Aalto University School of Engineering Department of Civil and Structural Engineering Building Materials Technology](https://reader033.vdocuments.pub/reader033/viewer/2022051602/5ae574737f8b9a8b2b8be1bc/html5/thumbnails/32.jpg)
Concrete Technology 2
SO3[%]
Cl-[%]
SiO2[%]
Na2O-equivalent
[%]
SiO2+Al2O3+Fe2O3
[%]
MgO[%]
CaO[%]
Loss ofignition([%])
Wood ash 1 8 0,4 35 4,1 35 + 18+ 3 = 56
3 15 C (7)
Wood ash 2 3 0,2 43 3,3 43 + 22+ 4 = 69
3 15 A (1)
Wood ash 3 10 1,3 20 4,9 20 + 14+ 4 = 38
3 31 A (2)
Wood ash 4 8 0,3 28 5,4 28 + 17+ 6 = 51
5 15 A (3)
Wood ash 5 2 0,2 36 3,7 36 + 29+ 2 = 67
2 14 B (5)
Limit valuesin
(SFS-EN450-1)
for fly ash
< 3,0 % < 0,1 % reactive> 25 %
< 5 % > 70 % < 4 % free< 2,5 %react.
< 10 %
A < 5 %B 5-7 %C 7-9 %
![Page 33: Concrete Technology 2/4 - Aalto · Concrete Technology 2/4 Aalto University School of Engineering Department of Civil and Structural Engineering Building Materials Technology](https://reader033.vdocuments.pub/reader033/viewer/2022051602/5ae574737f8b9a8b2b8be1bc/html5/thumbnails/33.jpg)
Concrete Technology 2
![Page 34: Concrete Technology 2/4 - Aalto · Concrete Technology 2/4 Aalto University School of Engineering Department of Civil and Structural Engineering Building Materials Technology](https://reader033.vdocuments.pub/reader033/viewer/2022051602/5ae574737f8b9a8b2b8be1bc/html5/thumbnails/34.jpg)
Concrete Technology 2
![Page 35: Concrete Technology 2/4 - Aalto · Concrete Technology 2/4 Aalto University School of Engineering Department of Civil and Structural Engineering Building Materials Technology](https://reader033.vdocuments.pub/reader033/viewer/2022051602/5ae574737f8b9a8b2b8be1bc/html5/thumbnails/35.jpg)
Properties
Concrete Technology 2
Density[kg/ dm3]
Powder density[kg/dm3]
Activityindex28 d
Expansionof paste
14 d[µm]
Settingtime[min]
Wood ash1 2,79 0,69-0,72 0,86 67
Wood ash2 2,61 0,85-0,87 0,61 13
Wood ash3 3,00 0,95-0,97 0,84 64 210
Wood ash4 2,77 0,75-0,78 0,75 60
Wood ash5 2,62 0,68-0,72 0,83 30 225
Fly ash 0,96 54
Class B 2,22 240Class C 2,14
Portlandcement 1 84 200
![Page 36: Concrete Technology 2/4 - Aalto · Concrete Technology 2/4 Aalto University School of Engineering Department of Civil and Structural Engineering Building Materials Technology](https://reader033.vdocuments.pub/reader033/viewer/2022051602/5ae574737f8b9a8b2b8be1bc/html5/thumbnails/36.jpg)
Compressive strength
Concrete Technology 2
![Page 37: Concrete Technology 2/4 - Aalto · Concrete Technology 2/4 Aalto University School of Engineering Department of Civil and Structural Engineering Building Materials Technology](https://reader033.vdocuments.pub/reader033/viewer/2022051602/5ae574737f8b9a8b2b8be1bc/html5/thumbnails/37.jpg)
Compressive strength
![Page 38: Concrete Technology 2/4 - Aalto · Concrete Technology 2/4 Aalto University School of Engineering Department of Civil and Structural Engineering Building Materials Technology](https://reader033.vdocuments.pub/reader033/viewer/2022051602/5ae574737f8b9a8b2b8be1bc/html5/thumbnails/38.jpg)
Freeze-thaw durability
Quality control
Concrete Technology 2