Product Characteristics Major Applications
・Both shiny side Copper Foil with equal roughness on the two sides.
・Anode material for secondary Li-ion battery.
Product Specification
CBFLI-ION BATTERY USE COPPER FOIL
Items Unit Value Testing method
Nominal Thickness μm 8 10 12 IPC-TM-650
Thickness by weight g/m2 75 ±10% 85 ±10% 105 ±10% IPC-TM-650
Tensile Strength
at 23℃ kg/mm2 >40 >40 >40IPC-TM-650
at 180℃ kg/mm2 >8 >10 >10
Elongationat 23℃ % >2 >2 >2
IPC-TM-650at 180℃ % >3 >5 >8
Roughness of Shiny side (Rz) μm <1.6 <1.6 <1.6IPC-TM-650
Roughness of Matte side (Rz) μm <1.6 <1.6 <1.6
Matte side SEM image
CHANG CHUN PETROCHEMICAL CO., LTD.H.Q.: 301 SONGKIANG RD., 7TH FL., TAIPEI 104, TAIWANTEL: 886-2-2500-1800FAX: 886-2-2501-8018WEB SITE: www.ccp.com.tw
CCP長 春
COPPER FOIL
Drum side SEM image
HTEHIGH TEMPERATURE ELONGATION COPPER FOIL
Product Specification
Product Characteristics Major Applications
・Single side treated Copper Foil following IPC-4562 class 3.
・Surface plated with Zn/Cr.
・Glass Fiber Copper Clad Laminates ( FR-4, CEM-1, CEM-3, High Tg, HF )・Multi-layer Printed Circuit Board.
Items Unit Value Testing method
Nominal Thicknessμm 12 18 35 70
IPC-TM-650oz 1/3 1/2 1 2
Thickness by weight g/m2 107±10% 153±10% 305±10% 610±10% IPC-TM-650
Purity % >99.8 >99.8 >99.8 >99.8 IPC-TM-650
Tensile Strength
at 23℃ kg/mm2 >21 >21 >28 >28IPC-TM-650
at 180℃ kg/mm2 >15 >15 >15 >15
Elongationat 23℃ % >3 >4 >5 >5
IPC-TM-650at 180℃ % >2 >3 >3 >3
Roughness of Shiny side (Ra) μm <0.43 <0.43 <0.43 <0.43 IPC-TM-650
Roughness of Matte side (Rz) μm <7 <8 <10 <14 IPC-TM-650
Peel Strengthkg/cm >1.1 >1.3 >1.7 >1.9
IPC-TM-650lb/in >6.0 >7.3 >9.5 >10.6
COPPER FOIL
CHANG CHUN PETROCHEMICAL CO., LTD.H.Q.: 301 SONGKIANG RD., 7TH FL., TAIPEI 104, TAIWANTEL: 886-2-2500-1800FAX: 886-2-2501-8018WEB SITE: www.ccp.com.tw
CCP長 春
Peel Strength Tested with Standard FR-4 material(6 sheets 7628P Prepreg)
Matte side SEM image Shiny side SEM image
DSTFD R U M S I D E T R E A T E D F O I L
Major ApplicationsProduct Characteristics・Copper Foil with treatment on
Drum side.・Inner layer application using low
profile foils・Suitable for fine patterns.
Product Specification
Items Unit Value Testing method
Nominal Thicknessμm 18 35 70
IPC-TM-650oz 1/2 1 2
Thickness by weight g/m2 153±10% 305±10% 610±10% IPC-TM-650
Purity % >99.8 >99.8 >99.8 IPC-TM-650
Tensile Strength
at 23℃ kg/mm2 >21 >28 >28IPC-TM-650
at 180℃ kg/mm2 >15 >15 >15
Elongationat 23℃ % >4 >5 >5
IPC-TM-650at 180℃ % >3 >3 >3
Roughness of treated side (Rz) μm <5.0 <5.0 <5.0 IPC-TM-650
Roughness of Matte side (Rz) μm <6.0 <8.0 <10.0 IPC-TM-650
Peel Strengthkg/cm >0.8 >0.8 >0.9
IPC-TM-650lb/in >4.5 >4.5 >5.0
COPPER FOIL
CHANG CHUN PETROCHEMICAL CO., LTD.H.Q.: 301 SONGKIANG RD., 7TH FL., TAIPEI 104, TAIWANTEL: 886-2-2500-1800FAX: 886-2-2501-8018WEB SITE: www.ccp.com.tw
CCP長 春
Peel Strength Tested with Standard FR-4 material(6 sheets 7628P Prepreg)
Matte side SEM image Treated side SEM image
Product Characteristics Major Applications
・High Flexibility・High tensile strength・Very low profile・High peel strength
・Specialized for 2-Layers and 3-Layers Flexible Copper Clad Laminate(FCCL).
VLPV E R Y L O W P R O F I L E C O P P E R F O I L
Items Unit Value Testing method
Nominal Thickness μm 9 12 18 IPC-TM-650
Thickness by weight g/m2 79 ±10% 107 ±10% 153 ±10% IPC-TM-650
Tensile Strength
at 23℃ kg/mm2 >40 >40 >40 IPC-TM-650
at 180℃ kg/mm2 >10 >10 >10 IPC-TM-650
Elongationat 23℃ % >2 >2 >2 IPC-TM-650
at 180℃ % >3 >5 >8 IPC-TM-650
Roughness of Matte side (Rz) μm <3.0 <3.0 <3.0 IPC-TM-650
COPPER FOIL
Product Specification
CHANG CHUN PETROCHEMICAL CO., LTD.H.Q.: 301 SONGKIANG RD., 7TH FL., TAIPEI 104, TAIWANTEL: 886-2-2500-1800FAX: 886-2-2501-8018WEB SITE: www.ccp.com.tw
CCP長 春
Matte side SEM imageDrum side SEM image
Product Characteristics
Major Applications
・Copper foil containing Phenolic resin Adhesive.
・Paper Phenolic Copper Clad Laminates(FR-1, FR-2, HB).
・Single side Printed Circuit Boards.
LTLC O P P E R F O I L W I T H A D H E S I V E
Items Unit Value Testing method
Nominal Thicknessμm 18 35 70 IPC-TM-650
oz 1/2 1 2 IPC-TM-650
Thickness by weight g/m2 153±10% 305 ±10% 610 ±10% IPC-TM-650
Purity % >99.8 >99.8 >99.8 IPC-TM-650
Tensile Strength at 23℃ kg/mm2 >21 >28 >28 IPC-TM-650
Elongation at 23℃ % >2 >3 >3 IPC-TM-650
Roughness of Shiny side (Ra) μm <0.43 <0.43 <0.43 IPC-TM-650
Peel Strength kg/cm >1.2 >1.7 >1.9 IPC-TM-650
Adhesive content g/m2 24~29 24~29 30~35 JIS-C-6481
Volatile content % 1.5~4.0 1.5~4.0 1.5~4.0 JIS-C-6481
Surface resistance
C-96/20/65 Ω 1 x 1010 1 x 1010 1 x 1010 JIS-C-6481C-96/20/65+C-96/40/90 Ω 1 x 1010 1 x 1010 1 x 1010 JIS-C-6481
COPPER FOIL
Product Specification
CHANG CHUN PETROCHEMICAL CO., LTD.H.Q.: 301 SONGKIANG RD., 7TH FL., TAIPEI 104, TAIWANTEL: 886-2-2500-1800FAX: 886-2-2501-8018WEB SITE: www.ccp.com.tw
CCP長 春
Shiny side SEM image
Product Characteristics
Major Applications
・Copper foil containing Anti-Tracking Adhesive.
・Paper Phenolic Copper Clad Laminates(FR-1, FR-2)
・Single side Printed Circuit Boards.
LTCC O P P E R F O I L W I T H A D H E S I V E
Items Unit Value Testing method
Nominal Thicknessμm 18 35 70 IPC-TM-650
oz 1/2 1 2 IPC-TM-650
Thickness by weight g/m2 153±10% 305 ±10% 610 ±10% IPC-TM-650
Purity % >99.8 >99.8 >99.8 IPC-TM-650
Tensile Strength at 23℃ kg/mm2 >21 >28 >28 IPC-TM-650
Elongation at 23℃ % >2 >3 >3 IPC-TM-650
Roughness of Shiny side (Ra) μm <0.43 <0.43 <0.43 IPC-TM-650
Peel Strength kg/cm >1.2 >1.7 >1.9 IPC-TM-650
Adhesive content g/m2 30~34 30~34 33~37 JIS-C-6481
Volatile content % 1.0~3.5 1.0~3.5 1.0~3.5 JIS-C-6481
Surface resistance
C-96/20/65 Ω 1 x 1010 1 x 1010 1 x 1010 JIS-C-6481C-96/20/65+C-96/40/90 Ω 1 x 1010 1 x 1010 1 x 1010 JIS-C-6481
Tracking resistance drops >50 >50 >50 JIS-C-6481
COPPER FOIL
Product Specification
CHANG CHUN PETROCHEMICAL CO., LTD.H.Q.: 301 SONGKIANG RD., 7TH FL., TAIPEI 104, TAIWANTEL: 886-2-2500-1800FAX: 886-2-2501-8018WEB SITE: www.ccp.com.tw
CCP長 春
Shiny side SEM image