PENGACUANAN PENGACUANAN

SUNTIKANSUNTIKAN

(INJECTION (INJECTION

MOULDING)MOULDING)

CONTOH PRODUKCONTOH PRODUK

•PERHATIKAN RAJAH ASAS PROSES PENGACUANAN SUNTIKAN DAN JENIS JENIS MESIN PENGACUANAN SUNTIKAN

RAJAH 1-4 (A)

LANGKAH ASAS LANGKAH ASAS PENGACUANAN SUNTIKANPENGACUANAN SUNTIKAN

1. PELEBURAN RESIN2. PENYUNTIKAN RESIN YANG TELAH

LEBUR KE DALAM ACUAN TERTUTUP3. PENYEJUKAN RESIN DI DALAM

ACUAN TERTUTUP4. PEMBUKAAN ACUAN DAN

PENGELUARAN (EJECTION) PLASTIK TERACUAN

CONVENTIONAL INJECTION CONVENTIONAL INJECTION MOULDINGMOULDING

PISTON TYPE PISTON TYPE PREPLASTIFYINGPREPLASTIFYING

SCREW TYPE SCREW TYPE PREPLASTIFYINGPREPLASTIFYING

RECIPROCATING SCREW RECIPROCATING SCREW INJECTIONINJECTION

• SELALU DIGUNAKAN UNTUK TERMOPLASTIK ATAU TERMOSET TIDAK DIPERKUATKAN

• BOLEH JUGA DIGUNAKAN UNTUK MENGHASILKAN KOMPOSIT DIPERKUATKAN GENTIAN PENDEK DAN UNTUK TERMOSET

• PLASTIK YANG BIASA DIPROSES DENGAN TEKNIK INI IALAH PP, PA DAN PC

SLIDE SHOWSLIDE SHOW

ON 100 PERCENTON 100 PERCENT

KELEBIHAN PENGACUANAN KELEBIHAN PENGACUANAN SUNTIKANSUNTIKAN

• PRODUK BOLEH DIHASILKAN DENGAN PANTAS (KADAR PENGELUARAN TINGGI)

• PENGELUARAN ISIPADU TINGGI ADALAH MUNGKIN

• KOS BURUH YANG RENDAH PER UNIT MESIN

• PRODUK TIDAK MEMERLUKAN ‘FINISHING’

• PERMUKAAN, WARNA DAN

‘FINISHING’ YANG BERLAINAN BOLEH

DIHASILKAN

• PENGGUNAAN PELBAGAI PLASTIK

DAPAT DILAKUKAN TANPA PERLU

MENUKAR MESIN ATAU ACUAN

• UNTUK KEBANYAKAN REKABENTUK,

PROSES INI ADALAH PALING

EKONOMIK UNTUK DIHASILKAN

KEKURANGAN PENGACUANAN KEKURANGAN PENGACUANAN SUNTIKANSUNTIKAN

• INDUSTRI PLASTIK MEMPUNYAI KEUNTUNGAN YANG RENDAH (LOW PROFIT MARGIN)

• OPERASI TIGA SHIFT PERLU UNTUK BERSAING

• KOS ACUAN SANGAT TINGGI• MESIN DAN PERALATANNYA MAHAL• KAWALAN PROSES MUNGKIN TIDAK

BEGITU BAIK• PERALATAN TIDAK KONSISTEN SEMASA

BEROPERASI• KUALITI MUNGKIN AGAK SUKAR

DITENTUKAN SERTA MERTA

PROSES ASASPROSES ASAS

LEBURAN ATAU ‘PLASTICISED’ PLASTIK DI SUNTIK ATAU DIPAKSA KE DALAM ACUAN DI MANA IA DI SIMPAN SEHINGGA DIKELUARKAN DALAM KEADAAN PEPEJAL DAN MENYERUPAI KAVITI ACUAN YANG DIGUNAKAN

ACUAN MUNGKIN TERDIRI DARI SATU KAVITI ATAU BANYAK KAVITI (MULTI CAVITY) YANG BERBENTUK SAMA ATAU BERLAINAN, SETIAP SATU DISAMBUNGKAN DENGAN ‘CHANNEL’ ALIRAN ATAU ‘RUNNERS’ YANG MENGARAHKAN LEBURAN KE DALAM SETIAP KAVITI

PROSES INI ADALAH SALAH SATU KAEDAH YANG PALING EKONOMIK UNTUK PENGELUARAN PRODUK SECARA BESAR-BESARAN

SPRU, “RUNNER”, PINTU DAN KAVITISPRU, “RUNNER”, PINTU DAN KAVITI

TERDAPAT EMPAT (4) OPERASI TERDAPAT EMPAT (4) OPERASI ASAS:ASAS:

• MENINGKATKAN SUHU PLASTIK KE SUATU TAHAP IA AKAN MENGALIR DI BAWAH TEKANAN – PEMANASAN DAN PENCAMPURAN SECARA SERENTAK – MENGHASILKAN LEBURAN YANG SERAGAM SUHU DAN KELIKATAN. KESELURUHAN PROSES INI DIPANGGIL ‘PLASTICATION’ ATAU ‘PLASTICIZING’

• MEMBOLEHKAN LEBURAN PLASTIK MEMBEKU DALAM ACUAN YANG DITUTUP. LEBURAN PLASTIK DARI SILINDER SUNTIKAN DIPINDAHKAN MELALUI BEBERAPA ‘CHANNEL’ ALIRAN (RUNNER) KE DALAM KAVITI

• PENYEJUKAN• MEMBUKA ACUAN UNTUK MENOLAK

KELUAR (EJECTION) PLASTIK YANG TELAH MENJADI PEPEJAL DENGAN CARA MENGELUARKAN HABA DARI LEBURAN

OPERASI TADI AKAN MENENTUKAN PRODUKTIVITI KERANA KELAJUAN PENGELUARAN BERGANTUNG PADA BERAPA CEPAT PLASTIK DILEBURKAN, BERAPA CEPAT IA BOLEH DISUNTIK DAN BERAPA LAMA MASA UNTUK MENYEJUKKANNYA DALAM ACUAN – PUSINGAN PENYUNTIKAN

KOMPONEN ASAS UNTUK SISTEM KOMPONEN ASAS UNTUK SISTEM PENGACUANAN SUNTIKAN:PENGACUANAN SUNTIKAN:

• PENYEBATIAN• PENGERINGAN• PENYUAPAN• PEMETERAN• PLASTICATION (PELEBURAN)• PENYUNTIKAN• PENYEJUKAN • PENOLAKAN KELUAR (EJECTION)

URUTAN PERGERAKAN URUTAN PERGERAKAN MEKANIKAL UMUM SEMASA MEKANIKAL UMUM SEMASA

PEMPROSESAN:PEMPROSESAN:

• PENGAPIT (ACUAN) DITUTUP• RAM PENYUNTIKAN BERGERAK KE DEPAN

UNTUK MENYUNTIK LEBURAN• SKRU MENGEPAM KE BELAKANG APABILA

LEBURAN SEJUK DALAM ACUAN• SKRU BERHENTI BERPUTAR DAN PENGAPIT

DIBUKA• PLASTIK TERACUAN DITOLAK KELUAR DARI

ACUAN

Resin feed into the barrel

Shot accumulates here

CAVITY GETS FILLED

SCREW MOVES

FORWARD

COOLING LINES PRESSURE IS MAINTAINED IN CAVITY

MOULD IS OPENED

UNTUK MENDAPATKAN UNTUK MENDAPATKAN KEPUTUSAN YANG OPTIMUM BAGI KEPUTUSAN YANG OPTIMUM BAGI SESUATU PLASTIK DAN ACUAN :SESUATU PLASTIK DAN ACUAN :

• SUHU PELEBURAN• TEKANAN PENYUNTIKAN (INJECTION

PRESSURE)• KELAJUAN PENGISIAN ACUAN

(INJECTION SPEED)

SUHU PELEBURANSUHU PELEBURAN

• PLASTIK BERBEZA DARI SEGI KELIKATAN (PENGALIRAN – EASE OF FLOW) DAN MASALAH INI MENJADI LEBIH RUMIT DENGAN ADANYA GRED YANG PELBAGAI

• TAMBAHAN LAGI SIFAT PENGALIRAN PLASTIK ADALAH NON-NEWTONIAN (HUBUNGAN TIDAK LINEAR ANTARA TEKANAN DAN PENGALIRAN)

• SIFAT PENGALIRAN TIDAK BOLEH DIWAKILI OLEH SATU NILAI SAHAJA

CONTOH KELIKATAN PLASTIK CONTOH KELIKATAN PLASTIK PADA SUHU BERBEZAPADA SUHU BERBEZA

BAHAN(NYLON)

KELIKATAN PADA 1,000 s-1

240˚C 260˚C 280˚C 300˚C

1 98 78 63 50

2 149 115 89 69

3 394 319 259 210

CONTOH KELIKATAN PLASTIK CONTOH KELIKATAN PLASTIK PADA KADAR RICIH BERBEZAPADA KADAR RICIH BERBEZA

BAHAN KELIKATAN PADA SUHU 280˚C

100s-1 1000s-1 10000s-1 100,000s-1

1 197 63 20 6

2 323 89 25 7

3 1220 259 55 12

• DALAM KEBANYAKAN KES, PLASTIK ADALAH BERSIFAT PSEUDOPLASTIK IAITU MEREKA MENJADI KURANG LIKAT (SENANG MENGALIR) BILA DIGERAKKAN DENGAN CEPAT

• KELIKATAN BAHAN BERKURANG BILA KADAR RICIH DITINGKATKAN (PENGISIAN ACUAN LEBIH MUDAH)

• MENINGKATKAN SUHU LEBURAN AKAN KURANGKAN TEKANAN PENYUNTIKAN YANG DIPERLUKAN PADA KADAR PENGALIRAN TERTENTU

SUHU PENGACUANAN BEBERAPA JENIS SUHU PENGACUANAN BEBERAPA JENIS PLASTIKPLASTIK

TEKANAN TEKANAN PENYUNTIKANPENYUNTIKAN

• SEMASA PENGISIAN ACUAN, TEKANAN PENYUNTIKAN TINGGI PERLU UNTUK MENGEKALKAN KELAJUAN PENGISIAN ACUAN YG DIPERLUKAN

• BILA ACUAN TELAH PENUH, TEKANAN TINGGI TIDAK LAGI DIPERLUKAN

• MUNGKIN BOLEH GUNAKAN 2 PERINGKAT TEKANAN

KELAJUAN KELAJUAN PENYUNTIKANPENYUNTIKAN

(KELAJUAN PENGISIAN (KELAJUAN PENGISIAN ACUAN)ACUAN)

• BILA MENGACUANKAN PRODUK NIPIS, KELAJUAN TINGGI DIPERLUKAN UNTUK MEMENUHKAN ACUAN SEBELUM PEMBEKUAN BAHAN

• UNTUK MENDAPATKAN PERMUKAAN YANG BAIK BAGI PRODUK TEBAL, SUNTIKAN PERLAHAN DIGUNAKAN

• BAGI KEBANYAKAN MESIN, MASA UNTUK MENGISI ACUAN SELESAI DALAM MASA 1 SAAT

SAIZ MESINSAIZ MESIN• DARI BEBERAPA GRAM KEPADA BEBERAPA

PAUN (ADA YANG MENCAPAI HINGGA 395 PAUN, KEKUATAN PENGAPIT 10,000 TAN)

• ‘MINIATURE INJECTION MOULDING MACHINE’ (RAJAH). TERDAPAT BANYAK CABARAN UNTUK PERKEMBANGAN PADA MASA DEPAN. KEPERLUAN UNTUK ACUAN MIKRO:– PEMANASAN DAN PENYEJUKAN YANG CANGGIH– VAKUM UNTUK KAVITI– PENGESAN YANG KHUSUS– PERALATAN DENGAN KETEPATAN TINGGI

DIPERLUKAN

MINIATURE INJECTION MOULDING MINIATURE INJECTION MOULDING MACHINEMACHINE

• MESIN PENYUNTIKAN YANG SANGAT BESAR (LIHAT RAJAH). DISEBABKAN OLEH KEPERLUAN INDUSTRI AUTOMOTIF, PERKAKASAN & BANGUNAN, PEMBINAAN DAN LAIN-LAIN. PENGGUNAAN MASA KINI/DEPAN:– BADAN KERETA/PANEL– ALAT PERKAKASAN (PETI SEJUK DAN MESIN

BASUH)– BADAN BOT– KOLAM RENANG– MESIN YANG AGAK BESAR:

• HUSKEY E8000 • KEKUATAN PENGAPIT (CLAMP FORCE) 8000 TAN• SAIZ PLATEN: 19 X 16 X 13 KAKI• BERAT SUNTIKAN: 20 – 145 PAUN

MESIN PENGACUANAN SUNTIKAN YANG MESIN PENGACUANAN SUNTIKAN YANG BESARBESAR

KADAR PENYUNTIKANKADAR PENYUNTIKAN

• KADAR PENYUNTIKAN BOLEH DIPELBAGAIKAN

• LEBIH PANTAS MEMBOLEHKAN PENGACUANAN BENDA NIPIS DAN KURANGKAN MASA

• KEUPAYAAN KADAR PENYUNTIKAN BERGANTUNG KEPADA SAIZ MESIN – LEBIH BESAR MESIN LEBIH TINGGI KADAR PENYUNTIKAN

• KEUPAYAAN KADAR PENYUNTIKAN BERKADAR TERUS DENGAN PAM HIDROLIK. KADAR PENGALIRAN HIDROLIK DALAM GELEN PER MINIT MENENTUKAN KADAR PENYUNTIKAN

• TEKANAN HIDROLIK MENENTUKAN TEKANAN SUNTIKAN