PENGARUH THERMOCYCLING DAN PENAMBAHAN E- GLASS FIBER TERHADAP PENYERAPAN AIR
DAN STABILITAS WARNA BAHAN BASIS GIGITIRUAN NILON TERMOPLASTIK
QuickTime™ and a decompressor
are needed to see this picture.
TESIS
Oleh :
ARIYANI 117160021
PROGRAM PENDIDIKAN DOKTER GIGI SPESIALIS PROSTODONSIA FAKULTAS KEDOKTERAN GIGI
UNIVERSITAS SUMATERA UTARA MEDAN
2015
14
PENGARUH THERMOCYCLING DAN PENAMBAHAN E- GLASS FIBER TERHADAP PENYERAPAN AIR
DAN STABILITAS WARNA BAHAN BASIS GIGITIRUAN NILON TERMOPLASTIK
QuickTime™ and a decompressor
are needed to see this picture.
TESIS
Oleh :
ARIYANI 117160021
PROGRAM PENDIDIKAN DOKTER GIGI SPESIALIS PROSTODONSIA FAKULTAS KEDOKTERAN GIGI
UNIVERSITAS SUMATERA UTARA MEDAN
2015
15
PENGARUH THERMOCYCLING DAN PENAMBAHAN E- GLASS FIBER TERHADAP PENYERAPAN AIR
DAN STABILITAS WARNA BAHAN BASIS GIGITIRUAN NILON TERMOPLASTIK
QuickTime™ and a decompressor
are needed to see this picture.
TESIS
Diajukan sebagai Salah Satu Syarat untuk Memperoleh Gelar Spesialis Prostodonsia (Sp.Pros) dalam Bidang Ilmu Kedokteran Gigi pada Fakultas Kedokteran Gigi
Universitas Sumatera Utara
Oleh :
ARIYANI 117160021
PROGRAM PENDIDIKAN DOKTER GIGI SPESIALIS PROSTODONSIA FAKULTAS KEDOKTERAN GIGI
UNIVERSITAS SUMATERA UTARA MEDAN
2015
16
Judul Penelitian : Pengaruh thermocycling dan Penambahan E- Glass
Fiber terhadap Penyerapan Air dan Stabilitas Warna
Bahan Basis Gigitiruan Nilon Termoplastik
Nama Mahasiswa : Ariyani
Nomor Induk Mahasiswa : 117160021
Program Studi : Pendidikan Dokter Gigi Spesialis Prostodonsia
Fakultas Kedokteran Gigi
Universitas Sumatera Utara Medan
Menyetujui Pembimbing :
Prof.Ismet Danial Nst,drg.,Ph.D.,Sp.Pros(K)
Pembimbing Utama Pembimbing Anggota
Prof.Dr.Harry Agusnar,drs.,M.Sc.,MPhil
Ketua Program Studi, Dekan,
Prof.Haslinda Z Tamin,drg.,M.Kes.,Sp.Pros(K) Prof. H. Nazruddin, drg., C.Ort., Ph.D., Sp.Ort.
17
Telah diuji
Pada Tanggal : 4 Juni 2015
PANITIA PENGUJI TESIS
KETUA : Prof. Haslinda Z. Tamin, drg, M.Kes. Sp.Pros (K)
ANGGOTA : 1. Prof. Ismet Danial Nasution, drg., Ph.D., Sp.Pros (K)
2. Prof.Dr.Harry Agusnar,drs.,M.Sc.,M Phil
3. DR. Darwin Yunus, MS
4. Syafrinani, drg., Sp.Pros. (K)
5. Ricca Chairunnisa, drg., Sp.Pros.
PERNYATAAN
18
PENGARUH THERMOCYCLING DAN PENAMBAHAN E- GLASS FIBER TERHADAP PENYERAPAN AIR DAN STABILITAS
WARNA BAHAN BASIS GIGITIRUAN NILON TERMOPLASTIK
TESIS
Dengan ini saya menyatakan bahwa dalam tesis ini tidak terdapat karya yang pernah diajukan untuk memperoleh gelar kesarjanaan di suatu perguruan tinggi, dan sepanjang pengetahuan saya juga tidak terdapat karya atau pendapat yang pernah ditulis atau diterbitkan oleh orang lain, kecuali yang secara tertulis diacu dalam naskah ini dan disebutkan dalam daftar pustaka.
Medan, 4 Juni 2015
Ariyani
DAFTAR ISTILAH
19
Spektrofotometer UV = Spektrofotometer ultra violet
∆E = Nilai perubahan warna yang didapat dari
∆ E = ( ( ∆L)2 + (∆a)2 + (∆b)2)1/2.
CIE L*a*b* = Metode penentuan perubahan warna berdasarkan
The International Commission on Illumination yaitu
CIE- Commission Internationale de L’ Eclairage
L* = Lightness
a*b* = Color-opponent dimensions, based on nonlinearly
dimensions
E-glass fiber = Electrical glass fiber
Silane MPS = a monofunctional γ-
methacryloxypropyltrimethoxysilane (MPS)
ABSTRAK
20
Penggunaan bahan nilon termoplastik sebagai bahan basis gigitiruan berkembang pada masa sekarang ini, namun, disamping kelebihannya dalam hal estetis, bahan basis gigitiruan nilon termoplastik juga memiliki kelemahan, yaitu penyerapan air yang tinggi dan stabilitas warna yang rendah. Penyerapan air yang tinggi merupakan salah satu faktor ekstrinsik yang mempengaruhi stabilitas warna bahan basis nilon termoplastik. Salah satu metode untuk mengurangi penyerapan air adalah dengan penambahan E- glass fiber. Faktor lain yang mempengaruhi stabilitas warna adalah faktor intrinsik yaitu perubahan warna karena proses aging karena pada proses aging bahan terpapar kondisi fisikal dan kemikal dari adanya perubahan temperatur dan kelembaban. Metode simulasi in vitro untuk mengevaluasi sifat fisis dan mekanis bahan setelah proses aging adalah thermocycling. Thermocycling menyebabkan terjadinya hidrasi dari suatu bahan sehingga bahan tersebut mengabsorpsi air. Tujuan penelitian ini adalah untuk mengetahui pengaruh thermocycling dan pengaruh penambahan E-glass fiber terhadap penyerapan air dan stabilitas warna bahan basis gigitiruan nilon termoplastik tanpa dan dengan penambahan E-glass fiber yang tidak dan yang dilakukan thermocycling.
Jenis penelitian ini adalah eksperimental laboratoris. Pembuatan sampel bahan basis gigitiruan nilon termoplastik yang berjumlah 30 sampel dilakukan di Unit UJI Laboratorium Dental FKG USU. Kelompok sampel dibagi atas enam kelompok, yang terdiri dari kelompok tanpa E-glass fiber, dengan E-glass fiber 1% dan 1,5% yang tidak dan yang dilakukan thermocycling. Pengukuran nilai penyerapan air dilakukan menggunakan analytical balance dan pengukuran stabilitas warna dilakukan menggunakan alat spektrofotometer UV. Pengaruh thermocycling terhadap penyerapan air dan stabilitas warna dianalisis menggunakan uji T, dan pengaruh E glass fiber terhadap penyerapan air dan stabilitas warna dianalisis menggunakan uji ANOVA satu arah. Perbandingan pengaruh diantara kelompok tanpa E-glass fiber, dengan E-glass fiber 1% dan 1,5% yang tidak dan yang dilakukan thermocycling di analisis dengan uji LSD.
Hasil penelitian menunjukkan bahwa ada pengaruh thermocycling terhadap penyerapan air dan stabilitas warna pada kelompok tanpa E-glass fiber dan pada kelompok dengan penambahan E-glass fiber 1% dan 1,5%. Hasil uji ANOVA satu arah menunjukkan ada pengaruh penambahan E-glass fiber terhadap penyerapan air dan stabilitas warna bahan basis gigitiruan nilon termoplastik yang tidak dan yang dilakukan thermocycling.
Thermocycling sebanyak 2000 cycle merupakan simulasi kondisi rongga mulut selama 2 tahun pemakaian gigitiruan menunjukkan pengaruh terhadap penyerapan air dan stabilitas warna. E-glass fiber yang ditambahkan pada bahan basis gigitiruan juga berpengaruh terhadap penyerapan air dan stabilitas warna terlihat dari perubahan warna bahan basis gigitiruan yang ditambahkan E-glass fiber 1 % sampai 1,5 % pada kelompok yang di thermocycling secara klinis tidak terlihat dan dapat
21
diterima (∆E < 3,3), sedangkan pada kelompok yang tidak ditambahkan E-glass fiber perubahan warna secara visual terlihat jelas dan tidak dapat diterima (∆E > 3,3).
Kata kunci:thermocycling, E-glass fiber, penyerapan air,stabilitas warna,bahan basis gigitiruan nilon termoplastik
ABSTRACT
22
The utilization of nylon thermoplastic as denture base has developed at the present time, however, beside the superiority in esthetic aspect, nylon thermoplastic denture base material also has susceptibility which is high water absorption and low color stability. High water absorption is one of extrinsic factor that affect color stability of nylon thermoplastic denture base material. One of the methods to reduce water absorption is by addition of E-glass fiber. Another factor that affect water stability is intrinsic factor which is discoloration by aging process because in aging process the material is exposed to physical and chemical condition from temperature and humidity alteration. In vitro simulation method to evaluate physical and mechanical properties of the material after aging process is thermocycling. Thermocycling cause hydration of a material so that the material absorb water. The purpose of this research is to find out the effect of thermocycling and E-glass fiber addition to water absorption and color stability of nylon thermoplastic denture base material without and with E-glass fiber addition without and with thermocycling.
This is laboratory experimental type of research. 30 samples of nylon thermoplastic denture base material is fabricated in Unit UJI Laboratorium Dental FKG USU. The sample group was divided into 6 groups, consist of group without E-glass fiber, with 1% and 1,5% E-glass fiber without and with thermocycling. Measurement of water absorption value by using analytical balance and color stability measurement by using UV Spectrophotometer. The effect of thermocycling to water absorption and color stability is analyzed with T test and the effect of E-fiber to water absorption and color stability is analyzed with one way ANOVA test. The comparison of effect among group without E-glass fiber, with 1% and 1,5% E-glass fiber without and with thermocycling is analyzed with LSD test. Result shows that there is an effect of thermocycling to water absorption and color stability in group without E-glass fiber and group with addition of 1% and 1,5% of E-glass fiber. One way ANOVA test result shows that there is an effect of E-glass fiber addition to water absorption and color stability of nylon thermoplastic denture base material without and with thermocycling. Thermocycling with 2000 cycle is the simulation of oral cavity condition for 2 years denture usage shows an effect to water absorption and color stability. E-glass fiber addition to denture base material also affect water absorption and color stability as seen from discoloration of denture base material with the addition of 1% to 1,5% E-glass fiber in thermocycled group is not visible and acceptable (∆E < 3,3), while in group without E-glass fiber addition, discoloration is clearly seen visually and unacceptable (∆E > 3,3). Keywords: thermocycling, E-glass fiber, water absorption, color stability, nylon thermoplastic denture base material
KATA PENGANTAR
23
Puji dan syukur penulis panjatkan kepada Tuhan Yang Maha Esa yang telah
memberikan rahmat dan karunia-Nya, sehingga tesis ini dapat diselesaikan sebagai
salah satu syarat untuk memperoleh gelar Spesialis Prostodonsia pada Fakultas
Kedokteran Gigi Universitas Sumatera Utara.
Ucapan terima kasih yang sebesar-besarnya penulis sampaikan kepada Ibu
tersayang yaitu Drg Arida Yan Dallmer, suami tercinta, yaitu Muhammad Ibrahim,
SE dan anak-anakku tersayang, yaitu Nisa Amira Ibrahim dan Danial Adrian Ibrahim
yang telah memberikan kasih sayang yang tidak terbalas, doa, pengertian, semangat
dan dukungan baik moril maupun materiil kepada penulis sehingga penulis mampu
menyelesaikan pendidikan ini.
Dalam penulisan tesis ini, penulis telah banyak mendapat pengarahan serta
bimbingan dari berbagai pihak sehingga tesis ini dapat disusun dengan baik. Pada
kesempatan ini, dengan segala kerendahan hati , penulis ingin mengucapkan terima
kasih yang sebesar-besarnya kepada :
1. Prof. Ismet Danial Nasution, drg., Ph.D., Sp.Pros (K) sebagai dosen
pembimbing utama penulis yang telah banyak meluangkan waktu, tenaga dan dengan
penuh kesabaran membimbing penulis dalam menyelesaikan penulisan tesis ini.
Semangat, motivasi, arahan dan ilmu yang telah diberikan kepada penulis dengan
penuh ketulusan dan keikhlasan sangat berarti dalam proses penyelesaian tesis ini
khususnya serta membentuk pola berpikir penulis. Penulis tidak mampu membalas
seluruh bimbingan yang telah diberikan selama proses penyelesaian tesis ini, hanya
24
sebuah doa yang dapat penulis panjatkan agar kiranya Allah SWT memberikan
kesehatan, kekuatan, kebahagiaan dan keberkahan kepada Bapak agar tetap dapat
membimbing penulis dan seluruh residen program pendidikan dokter gigi spesialis
(PPDGS) Prostodonsia untuk menjadi spesialis Prostodonsia yang seutuhnya serta
tetap menjadi figur Bapak bagi seluruh residen PPDGS Prostodonsia FKS USU.
2. Prof. Dr. Harry Agusnar,drs.,M.Sc.,M Phil selaku dosen pembimbing
anggota dalam penulisan tesis ini yang telah meluangkan banyak waktu dan tenaga
untuk membimbing, memberikan pengarahan, semangat, motivasi serta dorongan
kepada penulis selama penulisan tesis ini hingga selesai. Penulis juga merasakan
pengorbanan dan pengertian dari Bapak selama pelaksanaan penelitian di University
of Chulalongkorn yang tidak dapat terlupakan. Untuk itu penulis hanya dapat
mendoakan kepada Allah SWT agar Bapak selalu diberikan kesehatan dan
keberkahan.
3. Prof. Haslinda Z. Tamin, drg., M.Kes., Sp.Pros (K) selaku Ketua Program
Studi (KPS) PPDGS Prostodonsia yang telah banyak meluangkan waktu,
mengarahkan, memberikan dorongan dan semangat serta solusi kepada penulis
selama penulisan tesis ini sehingga dapat diselesaikan dengan baik. Penulis juga
merasakan perhatian dan kasih sayang yang diberikan selama proses penyelesaian
tesis ini, untuk itu penulis hanya dapat membalas dengan memanjatkan doa kepada
Allah SWT agar Ibu tetap diberikan kesehatan, keberkahan dan umur yang panjang
agar Ibu tetap bisa menularkan semangat untuk tetap berbuat yang terbaik kepada
penulis khususnya dan residen PPDGS Prostodonsia umumnya.
25
4. Syafrinani, drg., Sp.Pros (K) selaku Ketua Departemen Prostodonsia
Fakultas Kedokteran Gigi Universitas Sumatera Utara dan anggota tim penguji tesis
yang telah banyak memberikan saran dan masukan, mengajarkan untuk bersabar dan
tenang dalam menghadapi semua masalah yang dijumpai penulis pada proses
penyelesaian tesis ini. Hanya sebuah doa yang dapat penulis panjatkan agar kiranya
Allah SWT memberikan umur yang panjang, dengan kesehatan yang prima sehingga
tetap menjadi figur ibu yang selalu memberikan semangat kepada penulis dan secara
umum untuk semua rekan PPDGS Prostodonsia FKG USU.
5. Prof. Nazruddin, drg., C.Ort., Ph.D., Sp.Ort., sebagai Dekan Fakultas
Kedokteran Gigi Universitas Sumatera Utara.
6. DR. Darwin Yunus, M.Sc selaku anggota tim penguji tesis yang telah
banyak memberikan saran dan masukan kepada penulis dalam menyelesaikan tesis
ini.
7. Ricca Chairunnisa, drg., Sp.Pros selaku anggota tim penguji yang telah
memberikan saran dan masukan kepada penulis dalam menyelesaikan tesis ini.
Ketenangan dan kesabarannya dalam menghadapi banyak pekerjaan serta kerendahan
hatinya yang telah memberikan semangat bagi penulis dalam menyelesaikan tesis ini.
8. Staf pengajar di Departemen Prostodonsia Fakultas Kedokteran Gigi
Universitas Sumatera Utara yang sedang menjalani pendidikan S2 di Universitas
Chulalongkorn, yaitu Andryas, drg., dan Hubban Nasution, drg., yang telah banyak
membantu penulis untuk dapat melakukan penelitian di Faculty of Dentistry,
University of Chulalongkorn, Bangkok, Thailand.
26
9. Seluruh pegawai dan pekerja di Unit UJI Laboratorium Dental FKG USU
yang telah banyak membantu dalam pembuatan sampel penelitian penulis sehingga
dapat selesai tepat pada waktunya.Terutama kepada saudara Muzakir dan Samsuri
yang telah meluangkan waktu untuk membantu menyelesaikan sampel penelitian
penulis sehingga penulis dapat menyelesaikan tesis ini dengan baik.
10. Direktur Dental Material Science Laboratorium Faculty of Dentistry
University of Chulalongkorn Bangkok Thailand, Associate Professor DR. Chaiwat
Maneenut yang telah memberikan ijin penggunaan alat spektrofotometer Ultra Scan
xe d65 kepada penulis.
11. Laboran Dental Material Science Laboratorium Faculty of Dentistry
University of Chulalongkorn Bangkok Thailand, Bapak Anucharte yang telah banyak
meluangkan waktu untuk membimbing penulis dalam mengoperasionalkan alat
spektrofotometer Ultra Scan xe d65.
12. DR. Djalil, MKM, yang telah membantu dalam analisis statistik data hasil
penelitian penulis.
13. Seluruh staf pengajar dan pegawai di Departemen Prostodonsia Fakultas
Kedokteran Gigi Universitas Sumatera Utara yang telah banyak memberikan saran
dalam penyelesaian tesis ini.
14. Sahabat-sahabat tersayang penulis : Sopan Sinamo,drg., Emerson Lim,
drg, Putri Welda, drg., MDSc, Suryanto Purba, drg. Mahasiswa S-1 (Tiffany dan
Vandersun) yang telah banyak membantu penulis dalam memberikan masukan dan
dorongan sehingga mempercepat penyelesaian tesis ini.
27
15. Rekan-rakan sejawat PPDGS Prostodonsia FKG USU Angkatan 2, 3, dan
4 yang selalu memberikan saran, semangat dan doa kepada penulis.
Penulis menyadari bahwa masih terdapat banyak kekurangan dalam penulisan
tesis ini, oleh karena itu, penulis mengharapkan kritik dan saran yang bersifat
membangun dari semua pihak.
Akhir kata penulis mengharapkan semoga tesis ini dapat memberikan
sumbangan pikiran yang berguna bagi pengembangan ilmu pengetahuan di Fakultas
Kedokteran Gigi Universitas Sumatera Utara, khususnya di Departemen
Prostodonsia.
Medan, 4 Juni 2015
Penulis,
(Ariyani, drg)
NIM: 117160021
28
DAFTAR RIWAYAT HIDUP
DATA PRIBADI
Nama : Ariyani, drg.,MDSc Pekerjaan : PNS sebagai staf pengajar pada Fakultas Kedokteran Gigi USU Medan Golongan : IIIc/ Lektor NIP : 19770905 200312 2 002 Alamat : Jl. DR. A Sofian No. 74 Kampus USU Medan Medan. JenisKelamin : Perempuan Agama : Islam No Kontak : 081263334530 Nama Ayah : Alm. Dr. Yan Dallmer Nama Ibu : Drg. Arida Yan Dallmer Nama Suami : M.Ibrahim, SE
PENDIDIKAN 1983 – 1989 : SD Kemala Bhayangkari I Medan 1989 – 1992 : SMP Negeri 1 Medan 1992 – 1995 : SMA Negeri 1 Medan 1995 – 2000 : Pendidikan Dokter Gigi FKG USU 2009 – 2012 : Pendidikan Magister Pasca Sarjana Kedokteran Gigi FKG USU Medan 2011 – Sekarang : Program Pendidikan Dokter Gigi Spesialis Prostodonsia FKG USU Medan
RIWAYAT PEKERJAAN
2001-2002 : Dokter Gigi PTT di PUSKESMAS Pembantu Pujidadi, Binjai 2003-Sekarang : Staf Pengajar pada Departemen Prostodonsia Fakultas Kedokteran Gigi USU Medan
KARYA ILMIAH YANG TELAH DIPRESENTASIKAN
29
NO JUDUL KEGIATAN TEMPAT/WAKTU 1. Key Principles of successful
Fixed Partial Denture Treatment For Endodontically Treated Abutment Teeth (Literature Review).
1 st Medan International Prosthodontic
(Inpro) Scientific Meeting.
JW Marriott Hotel, 30 Agustus -1
September 2012, Medan.
2. Peran E-Glass Fiber dan Thermocycling Terhadap Penyerapan Air dan Stabilitas Warna Bahan Basis Nilon Termoplastik: Tinjauan Pustaka. (The Role of E-Glass Fiber and Thermocycling in The Water Sorption and Colour Stability of Thermoplastic Nylon Base Material ).
3 rd Indonesian Prosthodontic
Scientific Meeting.
JW Marriott Hotel, 4-6 Oktober 2013,
Surabaya.
3. Modifikasi Teknik Pencetakan Fisiologis Kasus Edentulus Seluruhnya dengan Jaringan Flabby pada Anterior Rahang Atas : Laporan Kasus GTP (Modifications of Physiological Impression Technique for A Fully Edentulous Case With A Flabby Anterior Maxillary Ridge).
3 rd Indonesian Prosthodontic
Scientific Meeting.
JW Marriott Hotel, 4-6 Oktober 2013,
Surabaya.
4. Manajemen Estetik pada Kasus Agenesis Kongenital Insisivus Lateralis Rahang Atas (Aesthetisc Management of Congenital Agenesis Lateral Incisors with All- Ceramic Bridge).
Makassar Scientific Meeting V & Prosthodontic
Scientific Meeting Makassar.
Grand Clarion Hotel, 20-22 Maret 2014,
Makassar.
5. Modifikasi Teknik Pencetakan Fisiologis Kasus Edentulus Seluruhnya dengan Jaringan Flabby pada Anterior Rahang Atas : Laporan Kasus GTP (Modifications of Physiological Impression Technique for AFully Edentulous Case With A Flabby Anterior Maxillary Ridge).
10 Tahun Unit UJI Laboratorium Dental
FKG USU. (Bridging New
Concept of Dental Laboratory).
Hotel Santika Dyandra Convention, 7 Mei 2014,
Medan.
KARYA ILMIAH YANG TELAH DIPUBLIKASIKAN
30
NO JUDUL PUBLIKASI 1 Pengaruh Penambahan Fiber E-Glass
Reinforced Terhadap Penyerapan Air dan Stabilitas Warna Bahan Basis Gigitiruan Nilon Termoplastik
Dentika Dental Journal: Volume 17 Number 3 July 2013, ISSN 1693-671X
2 Peran E-Glass Fiber dan Thermocycling Terhadap Penyerapan Air dan Stabilitas Warna Bahan Basis Nilon Termoplastik: Tinjauan Pustaka. (The Role of E-Glass Fiber and Thermocycling in The Water Sorption and Colour Stability of Thermoplastic Nylon Base Material ).
Prosiding: 3 rd Indonesian Prosthodontic Scientific Meeting. (Bridging Sciences in Stomatognaatic System, Current and Update in Esthetic and Implant Dentistry). ISBN: 978-979-19022-2-9.
3 Modifikasi Teknik Pencetakan Fisiologis Kasus Edentulus Seluruhnya dengan Jaringan Flabby pada Anterior Rahang Atas : Laporan Kasus GTP (Modifications of Physiological Impression Technique for A Fully Edentulous Case With A Flabby Anterior Maxillary Ridge).
Prosiding: 3 rd Indonesian Prosthodontic Scientific Meeting. Prosiding: 3 rd Indonesian Prosthodontic Scientific Meeting. (Bridging Sciences in Stomatognaatic System, Current and Update in Esthetic and Implant Dentistry). ISBN: 978-979-19022-2-9.
PENGABDIAN YANG TELAH DILAKSANAKAN
NO JUDUL KEGIATAN TEMPAT/WAKTU 1. Peranan Gigitiruan
dalam Meningkatkan Kualitas Hidup Lansia.
- Penyuluhan Kesehatan Gigi dan Mulut
- Penyuluhan Cara Pemeliharaan Gigitiruan
- Pembuatan Gigitiruan Sebagian Lepasan dan Gigitiruan Penuh.
Upt Pelayanan Sosial Lanjut Usia dan Balita Wilayah Medan dan Binjai, Januari- Mei 2014, Binjai.
2. Meningkatkan Kualitas Hidup Lansia pada Yayasan Gereja GKPPD Resort Medan 1.
- Penyuluhan Kesehatan Gigi dan Mulut
- Penyuluhan Cara Pemeliharaan Gigitiruan
- Pembuatan Gigitiruan Sebagian Lepasan dan Gigitiruan Penuh.
Yayasan Gereja GKPPD Resort Medan 1 Juli-September 2014, Medan.
KURSUS YANG TELAH DIIKUTI
31
NO JUDUL KEGIATAN TEMPAT/WAKTU 1 How to Manage Your
Clinic. 1 st Medan International Prosthodontic (Inpro) Scientific Meeting.
JW Marriott Hotel, 30 Agustus -1 September 2012, Medan.
2 Table Clinic Demo for Prosthetic of Implant.
50 th Anniversary Faculty of Dentistry
University of Sumatera Utara.
JW Marriott Hotel, 27 Agustus 2011, Medan.
3 Immediacy in Advanced Implant Dentistry.
Immediacy in Advanced Implant
Dentistry.
JW Marriott Hotel, 19 July 2013, Medan.
4 Teknik Pembuatan Splin Oklusal.
10 Tahun Unit UJI Laboratorium Dental
FKG USU. (Bridging New Concept of Dental Laboratory).
Ruangan Seminar Departemen Prostodonsia FKG USU, 6 Mei 2014, Medan.
5 Update in Theories and Clinical Application of Dental Implant.
Update in Theories and Clinical Application of
Dental Implant.
JW Marriott Hotel, 18 Agustus 2014, Medan.
6 Esthetic Rehabilitation with Bonded Porcelain Laminate Veneer.
Kuliah Tamu dan Hands On
Emerald Hotel, 5 Desember 2014, Medan.
32
DAFTAR ISI
Halaman
DAFTAR ISTILAH .................................................................................... i
ABSTRAK .................................................................................................. ii
ABSTRACT ............................................................................................... iv
KATA PENGANTAR ............................................................................... v
DAFTAR RIWAYAT HIDUP .................................................................... x
DAFTAR ISI .............................................................................................. xiv
DAFTAR GAMBAR ................................................................................. xviii
DAFTAR TABEL ...................................................................................... xx
DAFTAR GRAFIK ..................................................................................... xxi
DAFTAR LAMPIRAN .............................................................................. xxii
BAB 1 PENDAHULUAN ...................................................................... 1
1.1 Latar Belakang .................................................................... 1 1.2 Permasalahan................................................................................... 8 1.3 Rumusan Masalah ........................................................................... 9 1.4 Tujuan Penelitian ............................................................................ 10 1.5 Manfaat Penelitian .......................................................................... 10 1.5.1 Manfaat Teoritis …………………………………………… 10 1.5.2 Manfaat Praktis...................................................................... 11 1.5.2.1 Manfaat Klinis.............................................. 11 1.5.2.2 Manfaat Laboratoris..................................... 11 BAB 2 TINJAUAN PUSTAKA .............................................................. 12 2.1 Basis Gigitiruan Polimer ................................................................ 12 2.1.1 Pengertian ............................................................................ 12 2.1.2 Syarat Bahan Basis Gigitiruan ............................................ 13
2.1.3 Klasifikasi Bahan Basis Gigitiruan Polimer ........... 15 2.2 Nilon Termoplastik ............................................................ 17 2.2.1 Pengertian ............................................................... 17 2.2.2 Manipulasi .............................................................. 19 2.2.3 Keuntungan dan Kerugian...................................... 20 2.2.4 Sifat … ................................................................... 22
33
2.3 Penyerapan Air ................................................................... 24 2.3.1 Alat Pengukuran Penyerapan Air ....................................... 29 2.3.2 Faktor yang Mempengaruhi Penyerapan Air ...................................................................................... 30 2.3.3 Akibat yang Ditimbulkan ................................................... 34 2.4 Stabilitas Warna ............................................................................. 36 2.4.1 Alat Pengukuran Warna ..................................................... 39 2.4.2 Faktor yang Mempengaruhi Perubahan Warna ................. 41 2.5 Fiber Glass ..................................................................................... 43 2.5.1 Pengertian ........................................................................... 43 2.5.2 Jenis .................................................................................... 43 2.5.3 Bentuk ............................................................................... 44 2.5.4 Komposisi dan Fungsi ........................................................ 46 2.6 Thermocycling ................................................................................ 53 2.7 Landasan Teori ............................................................................... 59 2.8 Kerangka Konsep ........................................................................... 60 2.9 Hipotesis Penelitian ........................................................................ 61 BAB 3 METODOLOGI PENELITIAN................................................. 62 3.1 Jenis dan Desain Penelitian ............................................... 62 3.2 Lokasi dan Waktu Penelitian ............................................ 62 3.2.1 Lokasi Pembuatan Sampel .................................... 62 3.2.2 Lokasi Pengujian Sampel ...................................... 62 3.2.3 Waktu Penelitian ................................................... 62 3.3 Sampel dan Besar Sampel Penelitian ................................ 63 3.3.1 Sampel Penelitian .................................................. 63 3.3.2 Besar Sampel Penelitian ........................................ 63 3.4 Variabel Penelitian ............................................................ 65 3.4.1 Identifikasi Variabel Penelitian ............................. 65 3.5 Defenisi Operasional ......................................................... 66 3.6 Alat dan Bahan Penelitian ................................................. 69 3.6.1 Alat Penelitian ....................................................... 69 3.6.1.1 Alat yang Digunakan untuk Menghasilkan Sampel Nilon Termoplastik Tanpa dan Dengan Penambahan E-glass Fiber .......... 69 3.6.1.2 Alat yang Digunakan untuk menguji Sampel ...................................................... 70 3.6.2 Bahan Penelitian.................................................... 71 3.7 Cara Penelitian .................................................................. 72 3.7.1 Persiapan Pembuatan Sampel Penelitian .............. 72 3.7.1.1 Pembuatan Sampel Nilon Termoplastik (Kelompok tanpa E-glass fiber) ........................... 72
34
3.7.1.2 Pembuatan Sampel Nilon Termoplastik Dengan Penambahan E-glass Fiber 1% dan 1,5% ............................................................... 78 3.7.2 Pengukuran Nilai Penyerapan Air ..................................... 81 3.7.3 Pengukuran Stabilitas Warna ............................................ 84 3.8 Kerangka Operasional Penelitian .................................................. 86 3.9 Analisis Data ................................................................................. 88 BAB 4 HASIL PENELITIAN ................................................................ 89
4.1 Pengaruh Thermocycling terhadap Penyerapan Air Bahan Basis Gigitiruan Nilon Termoplastik Tanpa dan dengan Penambahan E-glass fiber 1% dan 1,5% ........................... 89 4.2 Pengaruh Thermocycling terhadap Stabilitas Warna Bahan Basis Gigitiruan Nilon Termoplastik Tanpa dan dengan Penambahan E-glass fiber 1% dan 1,5% ........................... 95 4.3 Pengaruh Penambahan E-glass fiber 1% dan 1,5% terhadap Penyerapan Air Bahan Basis Gigitiruan Nilon Termoplastik yang Tidak dan yang Dilakukan Thermocycling ............... 102 4.4 Pengaruh Penambahan E-glass fiber 1% dan 1,5% terhadap Stabilitas Warna Bahan Basis Gigitiruan Nilon Termoplastik yang Tidak dan yang Dilakukan Thermocycling ............... 104
BAB 5 PEMBAHASAN ......................................................................... 107
5.1 Pengaruh Thermocycling terhadap Penyerapan Air Bahan Basis Gigitiruan Nilon Termoplastik Tanpa dan dengan Penambahan E-glass fiber 1% dan 1,5% ........................... 107 5.2 Pengaruh Thermocycling terhadap Stabilitas Warna Bahan Basis Gigitiruan Nilon Termoplastik Tanpa dan dengan Penambahan E-glass fiber 1% dan 1,5% ........................... 111 5.3 Pengaruh Penambahan E-glass fiber 1% dan 1,5% terhadap Penyerapan Air Bahan Basis Gigitiruan Nilon Termoplastik yang Tidak dan yang Dilakukan Thermocycling ............... 116 5.4 Pengaruh Penambahan E-glass fiber 1% dan 1,5% terhadap Stabilitas Warna Bahan Basis Gigitiruan Nilon Termoplastik yang Tidak dan yang Dilakukan Thermocycling ............... 120 5.5 Keterbatasan Penelitian ..................................................... 123
35
BAB 6 KESIMPULAN DAN SARAN .................................................. 124
6.1 Kesimpulan ........................................................................ 124 6.2 Saran .................................................................................. 125
DAFTAR PUSTAKA .................................................................................... 126
LAMPIRAN
36
DAFTAR GAMBAR
Gambar Judul Halaman
2.1 Nilon termoplastik semi crystalline dengan rantai linier ................... 17
2.2 Rumus kimia nilon 66 ........................................................................ 18
2.3 Mold dan basis gigitiruan nilon sebelum di poles ........................ 20
2.4 Alat injector ....................................................................................... 20
2.5 Sartorius analytical balance .............................................................. 30
2.6 Spektrofotometer UV (Hunter Lab Scan XE, Germany) ................... 41
2.7 Fiber glass bentuk batang .................................................................. 45
2.8 Fiber glass bentuk anyaman .............................................................. 45
2.9 Fiber glass bentuk potongan kecil ..................................................... 46
2.10 Alat thermocycling ............................................................................ 54
3.1 Sampel ................................................................................................ 63
3.2 Timbangan digital (Sartorius, Japan) ................................................ 70
3.3 Spektrofotometer UV (Hunter Lab Scan XE, Germany) ................... 70
3.4 Thermocycling machine ..................................................................... 71
3.5 Penanaman model induk pada kuvet bawah ...................................... 74
3.6 Nilon termoplastik di dalam cartridge ............................................... 75
3.7 Cartridge dimasukkan ke dalam furnace ........................................... 76
3.8 Nilon termoplastik diinjeksikan ke dalam kuvet ................................ 76
3.9 Sampel dikeluarkan dari kuvet ........................................................... 77
3.10 Pemegang sampel ............................................................................... 78
3.11 Silane coupling agent ......................................................................... 79
3.12 Sampel yang telah selesai dipoles ...................................................... 80
3.13 Proses desikasi dan pengukuran penyerapan air ................................ 82
3.14 Sampel yang di thermocycling ........................................................... 82
3.15 Sampel dimasukkan dalam inkubator ................................................ 83
37
3.16 Sampel diletakkan pada alat spektrofotometer .................................. 85
3.17 Background putih .............................................................................. 85
3.18 Background hitam ............................................................................. 85
3.19 Nilai L* a* b* terlihat pada monitor ................................................ 85
38
DAFTAR TABEL
Tabel Judul Halaman
3.1 Definisi operasional variabel bebas .................................................. 66 3.2 Definisi operasional variabel terikat ................................................. 67 3.3 Definisi operasional variabel terkendali............................................ 67 4.1 Nilai penyerapan air bahan basis gigitiruan nilontermoplastik tanpa dan dengan penambahan E-glass fiber 1% dan 1,5 ....................................................................................................... 92 4.2 Nilai penyerapan air pada bahan basis gigitiruan nilon termoplastik tanpa dan dengan penambahan E-glass fiber 1% dan 1,5% ............................................................................................. 95 4.3 Nilai perubahan warna bahan basis gigitiruan nilon termoplastik tanpa dan dengan penambahan E-glass fiber 1% dan 1,5% ................................................................................................... 98 4.4 Stabilitas warna bahan basis gigitiruan nilon termoplastik tanpa dan dengan penambahan E-glass fiber 1% dan 1,5% ................................................................................................... 101 4.5 Pengaruh penambahan E-glass fiber 1% dan 1,5% terhadap penyerapan air bahan basis gigitiruan nilon termoplastik yang tidak di thermocycling ........................................................................ 103 4.6 Pengaruh penambahan E-glass fiber 1% dan 1,5% terhadap penyerapan air bahan basis gigitiruan nilon termoplastik yang di thermocycling ................................................................................. 104 4.7 Pengaruh penambahan E-glass fiber 1% dan 1,5% terhadap stabilitas warna bahan basis gigitiruan nilon termoplastik yang tidak di thermocycling ........................................................................ 105 4.8 Pengaruh penambahan E-glass fiber 1% dan 1,5% terhadap stabilitas warna bahan basis gigitiruan nilon termoplastik yang di thermocycling ................................................................................. 106
39
DAFTAR GRAFIK
Grafik Judul Halaman
4.1 Nilai penyerapan air bahan basis gigitiruan tanpa E-glass fiber yang tidak di thermocycling dan yang di thermocycling ..................................................................................... 90
4.2 Nilai penyerapan air bahan basis gigitiruan dengan penambahan E-glass fiber 1% yang tidak di thermocycling dan yang di thermocycling ................................................................. 91
4.3 Nilai penyerapan air bahan basis gigitiruan dengan penambahan E-glass fiber 1,5% yang tidak di thermocycling dan yang di thermocycling ................................................................. 91
4.4 Nilai rerata dan standar deviasi penyerapan air bahan basis gigitiruan nilon termoplastik tanpa dan dengan penambahan E-glass fiber 1% dan 1,5% ................................................................. 93
4.5 Stabilitas warna bahan basis gigitiruan tanpa E-glass fiber yang tidak di thermocycling dan yang di thermocycling ..................................................................................... 96
4.6 Stabilitas warna bahan basis gigitiruan dengan penambahan E-glass fiber 1% yang tidak di thermocycling dan yang di thermocycling ..................................................................................... 97
4.7 Stabilitas warna bahan basis gigitiruan dengan penambahan E-glass fiber 1,5% yang tidak di thermocycling dan yang di thermocycling ..................................................................................... 98
4.8 Nilai rerata dan standar deviasi stabilitas warna bahan basis gigitiruan nilon termoplastik tanpa dan dengan penambahan E-glass fiber 1% dan 1,5% ................................................................. 99
40
DAFTAR LAMPIRAN
Lampiran
1 Data nilai penyerapan air
2 Data nilai perubahan warna
3 Hasil uji statistik
4 Surat Ethical Clearence
5 Surat keterangan telah melakukan penelitian