materials of our products

　 Item Unit 995-FMG

995-FFG

99 97AZ95-ＦＦＧZ-243Z-300

Z-1001

MZ-15

MAG-2

MAG-4

MAG-21

　Physical properties

Apparent specific　gravity

- 3.98 3.98 3.91 3.88 4.00 5.62 5.93 5.74 3.82 3.56 3.61 3.61

Bulk specificgravity

－ 3.25 3.27 3.30 3.28 3.35 4.12 4.34 4.15 3.08 2.94 2.83 2.85

Apparent porosity ％ 18.3 18.0 15.6 15.6 17.3 26.9 26.8 27.7 19.3 17.4 21.6 21.3

M.O.R.at R.T. MPa 17.7 22.5 55.0 93.1 12.6 19.1 21.1 47.1 7.4 22.6 15.7 17.3

at 1200℃ MPa 12.7 15.0 24.0 37.1 10.0 10.3 23.0 24.5 18.1 17.7 11.8 13.4

Thermal expansion coefficient (R.Ｔ .～ 1000℃)

×10-6 /℃ 8.3 －－－ 8.9 8.8 8.8 8.8 - 13.5 13.7 13.7

Thermal conductivity(at 1000℃)

W /m・K

2.9 －－－ 2.6 1.4 - 1.4 - 3.7 3.5 3.5

Chemical composition

Al2O3 ％ 99.8 99.8 98.9 97.8 95.0 － - － 5.2 －－－

SiO2 ％ 0.05 0.05 0.8 2.0 0.1 0.1 0.1 0.1 0.1 3.0 0.2 0.1

Fe2O3 ％ 0.05 0.05 0.05 　－ 0.05 0.05 0.05 0.05 0.1 0.1 0.1

Na2O ％ 0.05 0.05 0.05 0.1 －－－ - －－－

ZrO2 ％－－－－ 4.5 94.5 89.8 94.7 14.2 －－－

Y2O3 ％ - - - - - 9.7 - - - - -

CaO ％－－－－ 0.2 4.9 - 4.5 0.3 0.3 0.3 0.3

MgO ％－－－－－－ - － 79.8 96.1 99.2 99.2

Materials of our products

※数値は代表値であり、規格値ではありません。

Item Unit 995-C 5035-2CKE-103CM-

1289CA-98C A-96G HA-P1

Physical properties


- 3.98 3.50 3.60 3.11 3.80 3.78 3.91

Bulk specific gravity

－ 3.20 2.75 2.98 2.52 3.80 3.78 3.91

Apparent porosity ％ 20.0 21.5 17.2 18.9 0 0 0

M.O.R.at R.T. MPa 25.0 12.7 14.7 16.8 284 284 382at 1200℃ MPa 18.0 13.7 17.7 14.7 －－－

Modulus of　Elasticity

Gpa －－－－ 314 294 373


×10-6 /℃ 8.3 6.0 6.3 4.8 7.9 7.7 7.9


W /m・K

2.9 2.3 2.4 2.1 －－－

Chemical Composition

Al2O3 ％ 99.8 88.6 90.8 76.1 98.0 95.7 99.6

SiO2 ％ 0.05 11.0 8.7 23.4 1.2 2.7 0.05

Fe2O3 ％ 0.05 0.1 0.1 0.1 0.6 0.7 0.11

Na2O ％ 0.05 0.2 0.1 0.2 － 0.7 －



Item Unit Y-1H Y-1 KS-1 KS-2 PA-8 ZE-22 ZE-35 KE-2 KE-9

Physical properties

　

Apparent specificgravity

- 3.98 3.98 3.58 3.70 2.91 5.68 5.25 3.46 3.52


－ 2.90 3.15 2.79 2.70 1.70 3.51 3.19 2.82 2.98

Apparent porosity

％ 27.1 20.6 22.1 27.2 56.7 38.3 39.2 18.5 15.3

M.O.R.at R.T. MPa 68.0 88.0 36.0 34.0 8.1 15.7 26.0 35.0 58.0at 1200℃

MPa －－－－－ 5.9 26.0 42.0 64.0


×10-6 /℃ －－－－－ 8.9 － 5.8 5.9


W /m・K

－－－－－ 1.5 － 2.3 2.4

　Chemicalcomposition

Al2O3 ％ 99.7 99.7 89.1 92.8 98.5 －－ 86.9 87.4

SiO2 ％ 0.05 0.05 10.7 7.0 1.0 0.1 0.1 12.7 12.1

Fe2O3 ％ 0.05 0.05 0.05 0.05 0.05 0.05 0.05 －－Na2O ％ 0.1 0.1 0.1 0.1 0.05 0.05 0.05 0.15 0.2

ZrO2 ％－－－－－ 94.5 85.2 －－CaO ％－－－－－ 5.0 3.7 －－MgO ％－－－－－－ 8,3 －－



Item Unit M-1289 B-100 B-102 B-201 B-111 B-211 S-10 S-12

Physical properties


－ 3.17 －－－－－－－


－ 2.62 1.53 1.55 1.50 1.55 1.53 1.02 1.21

Apparent porosity

％ 17.4 61 60 58 60 55 67 61

M.O.R.at R.T. MPa 12.7 10.8 11.8 6.2 9.8 6.0 2.9 4.9at 1200℃

MPa 11.8 5.9 4.4 8.8 4.0 8.0 1.0 2.0

Thermal expansion coefficient 　(R.Ｔ .～ 1000℃)

×10-

6 /℃4.9 8.3 8.2 7.8 8.2 7.9 5.0 5.0

Thermal conductivity (at 1000℃)

W /m・K

2.1 1.2 1.2 1.0 1.2 1.0 0.6 0.8


Al2O3 ％ 79.2 99.8 99.2 85.8 99.2 88.2 76.8 76.8

SiO ％ 20.4 0.05 0.6 13.9 0.6 11.4 22.6 22.6Fe2O3 ％ 0.1 0.05 0.05 0.05 0.05 0.05 0.1 0.1

Na2O ％ 0.2 0.05 0.05 0.1 0.1 0.1 0.2 0.2



Item UnitKE-

120SPKE-

164SPKE-701

KE-502

KE-503

KE-320

KE-130

KE-134

KE-103C

995-FMG

M-1289

Physicalproperties 　


　 -3.41 3.40 3.60 3.49 3.28 3.65 3.44 3.40 3.60 3.98 3.17


－　 2.98 2.94 2.93 2.91 2.70 3.00 2.85 2.90 2.98 3.25 2.62

Apparent porosity

　％ 12.6 13.6 18.6 16.8 17.6 17.8 17.3 14.9 17.2 18.3 17.4

M.O.R.

at R.T. MPa 12.3 13.7 6.5 10.0 13.1 11.8 11.8 13.7 14.7 17.7 12.7at 1200℃

MPa 13.2 14.7 7.6 13.1 15.3 15.7 13.7 16.8 17.7 12.7 11.8

at 1400℃

MPa 13.2 15.2 9.4 13.1 15.3 15.8 13.7 16.8 - - -

Thermal expansion coefficient(R.Ｔ .～ 1000℃)

×10-6 /℃ 5.6 5.6 5.7 5.7 - 5.7 5.6 5.6 6.3 8.3 4.9

Thermal conductivity(at1000℃)

W /m・K

2.3 2.3 2.4 2.4 - 2.4 2.3 2.3 2.4 2.9 2.1

Chemicalcomposition

Al2O3 ％ 85.3 85.1 90.7 88.1 82.9 92.6 86.3 85.7 90.8 99.8 79.2

SiO2 ％ 14.4 14.6 9.0 11.6 16.8 7.1 13.4 14.0 8.7 0.05 20.4

Fe2O3 ％ 0.05 0.05 0.05 0.05 0.05 0.05 0.05 0.05 0.1 0.05 0.1

Na2O ％ 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.1 0.05 0.2



Item Unit KE-F213 KE-F250 KE-F286 KE-F344 KE-F350

Physical properties 　


　 -3.41 3.50 3.53 3.55 3.63


－　 2.90 2.97 2.98 2.95 3.01

Apparent porosity

　％ 15.0 15.1 15.7 17.1 17.2

M.O.R.

at R.T. MPa 14.7 12.3 11.8 13.2 11.8at 1200℃

MPa 16.8 16.2 16.7 19.6 17.6

at 1400℃

MPa 16.8 16.2 16.7 19.6 17.2

Thermal expansion coefficient(R.Ｔ .～1000℃)

×10-

6 /℃5.7 5.7 5.7 5.7 5.7


W /m・K

2.4 2.4 2.4 2.4 2.4


Al2O3 ％ 86.1 88.3 88.4 89.0 92.2

SiO2 ％ 13.6 11.3 11.3 10.7 7.5

Fe2O3 ％ 0.05 0.05 0.05 0.05 0.05

Na2O ％ 0.2 0.2 0.2 0.15 0.15



Item UnitKE-

F426TKE-

F428TKE-

F429TKE-

F430TKE-

F431TKE-

F433KE-

F435KE-

F440KE-

F441KE-

F442KE-

F443KE-

F444KE-

F445

Physical properties


- 3.43 3.56 3.59 3.56 3.46 3.43 3.76 3.61 3.44 3.43 3.61 3.52 3.30


- 2.73 2.83 2.95 2.93 2.86 2.93 3.08 2.80 2.69 2.72 2.85 2.74 2.69

Apparent porosity

％ 20.4 20.6 17.8 17.7 17.2 14.8 18.1 22.5 21.9 20.8 20.9 22.1 18.4

M.O.R.

at R.T. MPa 10.4 12.8 11.0 10.3 11.6 15.1 14.8 15.8 15.0 7.7 7.2 16.9 28.9at 1200℃

MPa 14.7 20.1 12.4 10.6 16.6 17.2 21.4 19.2 19.0 8.9 9.1 20.1 33.1

at 1400℃

MPa 15.0 20.9 12.9 11.5 14.5 17.3 19.1 18.2 19.2 9.2 10.1 20.3 33.6

Thermal expansion coefficient(R.Ｔ .～1000℃)

×10-6 /℃ 5.6 5.7 5.7 5.7 5.6 5.5 5.7 5.7 5.5 5.5 5.7 5.7 5.0


W /m・ K

2.4 2.4 2.4 2.4 2.4 2.4 2.4 2.4 2.4 2.4 2.4 2.4 2.4


Al2O3 ％ 85.8 89.1 90.3 89.5 86.0 86.1 95.4 90.9 86.3 86.2 91.0 88.4 83.7

SiO2 ％ 13.9 10.6 9.4 10.2 13.7 13.6 4.3 8.8 13.4 13.5 8.7 11.3 16.0

Fe2O3 ％ 0.05 0.05 0.05 0.05 0.05 0.05 0.05 0.05 0.05 0.05 0.05 0.05 0.05

Na2O ％ 0.15 0.15 0.15 0.15 0.15 0.15 0.15 0.15 0.15 0.15 0.15 0.15 0.15



materials of our products