INTRODUCTION
Squeeze casting, also known as liquid metal forging,
is a combination of casting and forging process.
The molten metal is poured into the bottom half of the
pre-heated die. As the metal starts solidifying, the upper half closes
the die and applies pressure during the solidification
process.
Both ferrous and non-ferrous materials can be
produced using this method.
-
8/12/2019 910012408023
2/10
-
8/12/2019 910012408023
3/10
MATERIALS
ALUMINIUM:
Aluminium is a very light metal with a specific weight of 2.7
g/cm. For example, the use of aluminium in vehicles reduces dead-
weight and energy consumption while increasing load capacity. Its
strength can be adapted to the application required by modifying the
composition of its alloys.
STEEL:
Steel is a common material for building and forming. It makes
up the frames of cars, and it's used to make a variety of machine parts.However, steel comes in a number of varieties, and one of these types
is called low-carbon steel, which has different properties than those of
other types of steel.
-
8/12/2019 910012408023
4/10
LITERATURE SURVEY
C.S. Goh , K.S. Soh , P.H. Oon , B.W. Chua(2009)
Effect of squeeze casting parameters on the
mechanical properties of AZ91Ca Mg alloys.
A study on the effect of squeeze casting parameterson the mechanical properties of AZ91 Mg alloy with
2 wt.% Ca incorporated was conducted.
A good combination of tensile and macro hardness
properties was obtained with better mechanical
properties.
-
8/12/2019 910012408023
5/10
E. Hajjari a,M. Divandari b, A.R.Mirhabibi(2009)
The effect of applied pressure on fracture surface andtensile properties of nickel coated continuous carbon
fiber reinforced aluminum composites fabricated by
squeeze casting.
Reinforcing aluminum with carbon fibers, offers a
high potential for increasing the specific strength and
specific youngs modulus of these types of
composites. Therefore, carbon fiber reinforced
aluminum components are of great interest for the
potential aerospace and automotive applications.
-
8/12/2019 910012408023
6/10
D. Mandala, B.K.Duttab, S.C.Panigrahib(2007)
Effect of wt% reinforcement on microstructure and mechanicalproperties of Al2Mg base short steel fiber composites.
Al2Mg alloy composites with varying wt% of copper-coated
short steel fiber reinforced were prepared through liquid
process vortex method. Steel fibers were coated with copperby electroless deposition method. It is observed that density,
hardness and porosity increased with increasing wt% of fibers.
There is a significant improvement in strength and hardness
with addition of fibers.
-
8/12/2019 910012408023
7/10
Liu Lei,Li Weiwei, Tang Yiping, Shen Bin, Hu
Wenbin(2008)
Friction and wear properties of short carbon fiber
reinforced aluminum matrix composites.
The friction and wear properties of short carbonfibers (SCFs) reinforced aluminum matrix composite
were studied.
The incorporation of SCF in Al alloy improved thewear resistance greatly.
-
8/12/2019 910012408023
8/10
METHODOLOGY
The methodology for the reinforcement of steel in aluminium is as
follows.
Reinforcement of steel in aluminium
Selection of parameters
Samples casted by squeeze casting & Gravity die casting
Testing for mechanical & metallurgical properties
-
8/12/2019 910012408023
9/10
REFERENCE
Effect of squeeze casting parameters on themechanical properties of AZ91Ca Mg alloys C.S.Goh , K.S. Soh , P.H. Oon, B.W. Chu.
The effect of applied pressure on fracture surface and
tensile properties of nickel coated continuous carbonfiber reinforced aluminum composites fabricated bysqueeze casting E. Hajjari, M. Divandari, A.R.Mirhabibi.
Effect of wt% reinforcement on microstructure andmechanical properties of Al2Mg base short steelfiber composites D. Mandala, B.K. Duttab, S.C.Panigrahi.
-
8/12/2019 910012408023
10/10